PVA resin is a kind of heavy polymer. It is usually a white or slight yellow floccules, flake, granular or powdery in appearance.
PVA is non-toxic, insipid and non-polluting. PVA is a kind of water-soluble resin with good chemical stability. It also has good
adhesion, film-forming ability, insulation, oil resistance, abrasion resistance and gas barrier properties, and has typical
chemical properties of polyols and can make esterification, etherification, acetalization reactions.

Inquiry

Technical Parameters

Standard Grades
Hydrolyzed
Item
Viscosity
(mpa.s)
Alcoholysis
(mol)

Volatile

(%)
Sodium Acetate(%)

Ash

(%)
PH
Fully
04-99(L)
3.0-4.5
98.0-100.0
7.0
2.5
0.7
5-7
05-99(L)
4.0-6.0
98.0-100.0
7.0
2.5
0.7
5-7
10-99(L)
9.0-14.0
98.0-100.0
7.0
2.5
0.7
5-7
15-99(L)
20.0-26.0
98.0-100.0
7.0
2.5
0.7
5-7
17-98(L)
20.0-26.0
97.0-99.0
7.0
2.5
0.7
5-7
17-99(L)
20.0-26.0
98.0-100.0
7.0
2.5
0.7
5-7
17-99(H)
20.0-26.0
98.5-100.0
9.0
2.5
3.0
5-7
19-99(L)
26.0-32.0
98.0-100.0
7.0
2.5
0.7
5-7
19-99(H)
26.0-34.0
98.5-100.0
9.0
2.5
0.7
5-7
20-99(L)
32.0-40.0
98.0-100.0
7.0
2.5
0.7
5-7
20-99(H)
34.0-42.0
98.5-100.0
9.0
2.5
0.7
5-7
22-99(L)
40.0-48.0
98.0-100.0
7.0
2.5
0.7
5-7
23-99(H)
42.0-55.0
98.5-100.0
9.0
2.5
3.0
5-7
24-99(L)
48.0-60
98.0-100.0
7.0
2.5
0.7
5-7
26-99(L)
60.0-75.0
98.0-100.0
7.0
2.5
3.0
5-7
28-99(L)
75.0-90.0
98.0-100.0
7.0
2.5
0.7
5-7
Partially
04-88(L)
3.0-4.5
86.0-90.0
7.0
2.5
0.7
5-7
05-88(L)
4.0-6.0
86.0-90.0
7.0
2.5
0.7
5-7
17-80(L)
18.0-24.0
86.0-90.0
7.0
2.5
0.7
5-7
17-88(L)
20.0-28.0
86.0-90.0
7.0
2.5
0.7
5-7
20-88(L)
28.0-40.0
86.0-90.0
7.0
2.5
3.0
5-7
24-88(L)
40.0-55.0
86.0-90.0
7.0
2.5
0.7
5-7
Intermediate
10-92(L)
8.0-13.0
90.0-94.0
7.0
2.5
0.7
5-7
14-92(L)
13.0-18.0
90.0-94.0
7.0
3.5
0.7
5-7
17-92(L)
20.0-30.0
90.0-94.0
7.0
4.5
0.7
5-7
17-95(L)
20.0-30.0
94.0-96.0
7.0
5.5
0.7
5-7
17-96(L)
20.0-30.0
94.0-98.0
7.0
6.5
0.7
5-7
17-97(L)
21.0-31.0
96.0-98.0
7.0
7.5
0.7
5-7
Fine Particle Grades(S-Grade)
Item
Mesh size
Viscosity
(mpa.s)
Alcoholysis
(mol)
Volatile(%)
Sodium Acetate
(%)
Ash(%)
PH
04-88 S80
80
3.0-4.5
86.0-90.0
7.0
2.5
0.7
5-7
17-99 S120
120
20.0-26.0
98.0-100.0
7.0
2.5
0.7
5-7
17-99 S80
80
20.0-26.0
98.0-100.0
7.0
2.5
0.7
5-7
17-99 S50
50
20.0-26.0
98.0-100.0
7.0
2.5
0.7
5-7
05-88 S80
80
4.0-6.0
86.0-90.0
7.0
2.5
0.7
5-7
17-80 S80
80
18.0-24.0
86.0-90.0
7.0
2.5
0.7
5-7
20-88 S80
80
28.0-40.0
86.0-90.0
7.0
2.5
3.0
5-7
24-88 S80
80
40.0-55.0
86.0-90.0
7.0
2.5
0.7
5-7
Fiber Grade
specification
17-99F(H)
17-99F(L)
26-99F(L)
Alcoholysis %(mol)
99.8-100
99.8-100
99.8-100
Viscosity % ≤
9.0
7.0
7.0
Sodium Hydroxide % ≤
0.30
0.30
0.30
Residual Acetic Acid % ≤
0.20
0.20
0.20
Sodium HAcetate % ≤
7
2.5
2.5
Purity % ≥
84.7
92.0
92.0
Transparency % ≥
90.0
90.0
90.0
Coloring Degree % ≥
84.0
86.0
86.0
Swelling Capacity %
190±15
145±15
145±15
Average Degree of Polumerization
1750-1900
1750-1900
2450-2650
Molecular Weight
77000-83600
77000-83600
107800-116600
Appearance
White flocculent
White flake
White flake
Customized Grade
(Products are customized to meet special requirements for companies that have special applicationor that require to reach special performance. )
The following speciation item can be improved or modified .
Viscosity
(mpa.s)
Alcoholysis
(mol)
Volatile(%)
Sodium Acetate
(%)
Ash(%)
PH

Application

  • Add water at room temperature in the dissolving tank. Start the agitator, slowly add calculated amount of PVA into the tank. Keep PVA swelling in the water at room temperature for about 30min, and then raise the temperature of the PVA aqueous solution, when the temperature reaches 90-95℃, keep the temperature for 1-2hours. PVA can completely dissolve.

Package

25KGS/ BAG